VACCUM BAGGING FILM

Vacuum Bagging Film

LEADGO developed a wide range of vacuum bagging film for many applications.

They are suitable for wet lay-up, resin infusion and pre-preg processing up to temperatures of 230°c.

We are able to produce vacuum bagging films up to 12m wide, mostly used for marine and wind energy structures (blade, nacelle, boat, automotive…).

LVBF300B-1 - Co-extruded - 120°C - 75µ - Up to 10m

Multilayer co-extruded vacuum bagging film for low temperature vacuum application, widely used in marine and wind energy industries. It has two-sided off-form property.

  • Max temperature: 120°C
  • Thickness: 75 microns
  • Up to 10m

Download the LVBF300B-1 Technical Data Sheet

LVBF600Y - Co-extruded - 150°C - 50µ/65µ/75µ - Up to 12m

Multilayer co-extruded vacuum bagging film for low temperature vacuum application, widely used in marine and wind energy industries. It is not suitable for autoclave cure process.

  • Max temperature: 150°C
  • Thickness: 50, 65, 75 microns
  • Up to 12m

Download the LVBF 600Y Technical Data Sheet

LVBF150G - Co-extruded - 160°C - 75µ/90µ - Up to 10m

LVBF 150G is a multilayer co-extruded vacuum bagging film with releasing function ,widely used in marine and wind energy industries.

  • Max temperature: 160°C
  • Thickness: 90 microns
  • Up to 10m

Download the LVBF150G Technical Data Sheet

LVBF165B - Co-extruded - 165°C - 55µ/65µ/75µ - Up to 6.5m

Multilayer co-extruded vacuum bagging film for medium/low temperature vacuum application, widely used for marine and wind energy structures.

  • Max temperature: 165°C

  • Thickness: 55, 75 microns

  • Up to 6.5m

Download the LVBF165B Technical Data Sheet

LVBF350V - Co-extruded - 160°C - 75µ - Up to 5.5m

Multilayer co-extruded vacuum bagging film with polyolefin and nylon layer, it has high barrier property, suited for use with epoxy and phenolic system.

  • Max temperature: 160°C
  • Thickness: 50, 75 microns
  • Up to 5.5m

Download the LVBF350V Technical Data Sheet

LVBF250V - Co-extruded - 170°C - 75µ - Up to 10.5m

Multilayer co-extruded vacuum bagging film with polypropylene layer, it has high barrier property suited for use with epoxy and phenolic system.

  • Max temperature: 170°C
  • Thickness: 75 microns
  • Up to 10.5m

Download the LVBF250V Technical Data Sheet

LVF200G - Mono nylon - 205°C - 50µ/75µ - Up to 3.9m

Produced from modified Nylon resin, it is suitable for epoxy and phenolic resin. Recommended as a bagging film for advanced composites fabrication and other high-temperature/pressure application where softness, workability, pinhole-free and defect-free film are essential.

  • Max temperature: 205°C
  • Thickness: 50, 75 microns
  • Up to 3.9m

Download the LVF200G Technical Ddata Sheet

LVF230B - Mono nylon - 230°C - 55µ/75µ - Up to 3.04m

Produced from modified Nylon resin, it is suitable for epoxy and phenolic resin. Recommended as a bagging film for advanced composites fabrication and other high-temperature/pressure application where softness, workability, pinhole-free and defect-free film are essential.

  • Max temperature: 230°C
  • Thickness: 55/75 microns
  • Up to 3.04m

Download the LVF230B Technical Data Sheet