Peel Ply
LEADGO developed a full range of peel ply to meet customer requirement. Our Peel ply is free of any release agent or pollution and can be used directly on the surface of the part. After curing it peels quite easily without any residue or small pieces left on the part.
This high quality peel ply has been widely used in wind, marine and large parts production markets.
- Polyester (Excellent with phenolic resin)
- Nylon PA6 (Economical version)
- Nylon PA66 (High quality Peel ply)
R90HA - Polyester - 85g/m² - 180°C
Excellent strength Polyester peel ply.
It has been heat scoured and stabilized at high temperature. There is a red tracer yarn each 30mm. This high quality peel ply has been widely used in wind, marine and large parts production markets.
- Colour: White with red tracer
- Weight: 85 g/m²
- Width: Up to 1.80m
- Temperature max: 180°C
R60 - Nylon PA66 - 60g/m² - 205°C
Excellent porous Nylon66 peel ply or release fabric. It is our tightest weave nylon peel ply that produces a “fine” texture. R60 is free of any release agent or pollution and can be used directly on the surface of the part.
- Colour: White
- Weight: 60 g/m²
- Width: Up to 1.80m
- Temperature max: 200°C
R60S - Nylon PA66 - 60g/m² - 205°C - Silicone coated
Nylon 66 peel ply impregnated with a release agent. It can provide good peel property and can be used with most epoxy and polyester resin.
- Colour: Green
- Weight: 60 g/m²
- Width: Up to 1.80m
- Temperature max: 205°C
- Release agent: Silicone
R85PA66 - Nylon PA66 - 85g/m² - 205°C
Excellent porous Nylon 66 peel ply or release fabric. R85PA66 is free of any release agent or pollution and can be used directly on the surface of the part. After curing it peels quite easily without any residue or small pieces left on the part.
- Colour: White with red tracer
- Weight: 85 g/m²
- Width: Up to 1.80m
- Temperature max: 205°C
R92PA66 - Nylon PA66 - 92g/m² - 205°C
Pink porous Nylon 66 peel ply or release fabric. It has been heat scoured and stabilized at high temperature.
R92PA66 is free of any release agent or pollution and can be used directly on the surface of the part and will not pollute composite materials in the manufacturing process.
- Colour: Pink
- Weight: 92 g/m²
- Width: Up to 1.80m
- Temperature max: 205°C
KBB1N6 - Nylon PA6 - 85g/m² - 205°C
Excellent porous Nylon 6 peel ply or release fabric.KBB1N6 is free of any release agent or pollution and can be used directly on the surface of the part. After curing it peels quite easily without any residue or small pieces left on the part.
- Colour: White with red tracer or green
- Weight: 85 g/m²
- Width: Up to 1.80m
- Temperature max: 205°C
KBB3N6 - Nylon PA6 - 92g/m² - 205°C
Excellent porous Nylon 6 peel ply or release fabric. KBB3N6 is free of any release agent or pollution and can be used directly on the surface of the part. After curing it peels quite easily without any residue or small pieces left on the part.
- Colour: White with red tracer or Pink
- Weight: 92 g/m²
- Width: Up to 1.80m
- Temperature max: 205°C
KBB5N6 - Nylon PA6 - 105g/m² - 205°C
Excellent porous Nylon 6 peel ply or release fabric. KBB5N6 is free of any release agent or pollution and can be used directly on the surface of the part. After curing it peels quite easily without any residue or small pieces left on the part.
- Colour: White with red tracer or Pink
- Weight: 105 g/m²
- Width: Up to 1.80m
- Temperature max: 205°C
R85PA66AD - Nylon PA66 - 60g/m² - 180°C - Adhesive
Nylon 66 peel ply coated on one side with acrylic acid adhesive. It can provide good peel property and good adhesion performance that can be used with most epoxy and polyester resin.
- Colour: Green
- Weight: 60 g/m²
- Width: Up to 1.80m
- Temperature max: 180°C
- Release agent: Silicone
RF320PM - Porous PTFE coated glass - 260°C
Porous PTFE coated glass usefull to replace the peel ply for high temperature cures or for complex shapes parts.
- Colour: Brown
- Weight: 70g/m² or 138g/m²
- Width: Up to 1.25m
- Temperature max: 260°C